In the selection of NdFeB strong magnet coating, it is common to plating environment-friendly zinc and nickel. Some customers will ask when selecting the magnet coating that the nickel plating on the magnet (nickel copper nickel) can withstand the salt spray test for 48 hours, and I need to withstand the salt spray test for a longer time, such as 72 hours. Is nickel plating acceptable? Let's introduce it to you.
Can Nd-Fe-B magnet nicuni plating withstand salt spray test for 72 hours?
Nicuni plating is difficult. Some customers have high requirements for salt fog resistance and acid and alkali resistance, such as 72 hours resistance. At this time, Perrin coating can be selected, which is more guaranteed.
Ni-cu-Ni coating shaped special magnet;
Some people still have questions. Why not recommend epoxy?
Salt fog resistance 72 hours, nickel plating and epoxy are not guaranteed, so the recommendation of Parylene.
If you need salt fog resistance for 12 hours, zinc plating is recommended. At present, zinc plating can be divided into white zinc, blue zinc, blue zinc, color zinc and black zinc. At present, the market salt spray test of white zinc 16 hours: blue zinc 24 hours: color zinc 48 hours: black zinc 12 hours.
It is generally recommended that customers use nickel plating after 48 hours of salt spray. At present, the basic process of zinc plating is nickel-copper-nickel, which can ensure that the magnet is not damaged in the case of corrosion.
Above, we introduce to you whether Nd-Fe-B magnet nicuni plating can withstand 72 hours of salt fog test and the recommendation of customers for salt fog resistance hours. I hope it will be helpful to you.
More articles about neodymium magnet nickel plating;
Sintered Neodymium Magnet Chrome Coating VS Nickel Coating
Difference between magnet zinc and nickel coating in hardness, life and price
You are now seeing the specifications of this magnet ring OD 13mm, bore diameter 8mm, thickness of 3.5mm, the surface of the black epoxy, due to the reason of the photo may look like a ferrite, the actual bonded ring magnets, suitable for a variety of types of motor, sensor, and electric appliances....
Neodymium iron boron is divided into sintering, bonding and injection molding according to the different production processes. The general neodymium arc magnet is sintered, also called sintered arc neodymium magnet. Today this product is a bonded arc magnet that is not much used. The difference between sintered arc magnets is that bonded NdFeB magnet tiles require molds to produce....
Courage magnet manufacturers in China specialize in the production of various specifications of NdFeB strong magnetic tiles, large-radian strong magnetic tiles, large-sized arc magnetic tiles, arc-shaped sector magnets, and you are welcome to consult the arc-shaped magnets for quotation and proofing....
You are now browsing this ring for bonded neodymium magnets, gray epoxy on the surface, outer diameter 8mm, diameter of the hole is 4.5mm, height 6mm, it's mainly used in the field of electric motors, if you need other specifications, please consult us....
The sample shows a chemical nickel coated NdFeB small cylindrical magnet with N42 grade of magnetic properties, requires magnet N pole scribe marking, 2mm diameter, 2mm thickness, axial magnetization, the difference with conventional nickel is not obvious from the appearance but it is more suitable for use in wet, acidic or alkaline environments....
This is a small and thin (flat) round countersunk magnet, diameter 8mm, thickness is only 2mm, you see the countersunk hole neodymium magnets are generally about 3mm thick, so it belongs to the thinner countersunk hole magnets, if you want to be thinner it is difficult to process, for the customization of this type of magnets we are very good at,...
N42SH grade radial hollow cylindrical magnet 6.3x3x11mm for high speed motors...
This product is a T-shaped strong magnet, the material is rare earth NdFeB, it is a custom-shaped irregular Nd magnet, the sample is N52 grade, the surface is nickel coated, mainly used for connectors, electronic products, medical equipment, the maximum working temperature It is 80 degrees Celsius. If you need to use it in a high temperature environment, you need to replace the temperature resistant material....